Bright annealing of steels requires conditions that are reducing to steel oxides. Traditionally, the Ellingham diagram has been used to predict the conditions that correspond to oxidation of pure metals or reduction of their oxides. This method can be used to predict the conditions that should be reducing to iron oxides and the oxides of the alloying elements added to steels, such as chromium when stainless steels are considered. This traditional approach is not precise because it only uses thermodynamic data for pure metals and their oxides—it ignores the fact that iron and alloying elements form a solid solution. In addition, you can only determine the approximate equilibrium partial pressure ratio of hydrogen and water vapor for oxidation of a specific metal at a particular temperature.

Alternatively, you can use more accurate and convenient diagrams for steels and other alloys, which are created with the help of modern databases and computer programs, such as FactSage™ (thermochemical software and database package developed jointly between Thermfact/CRCT and GTT-Technologies) or Thermo-Calc software. Using the oxidation-reduction curves, presented as dew point of pure hydrogen or nitrogen-hydrogen atmospheres versus temperature, you can quickly select the atmosphere for annealing steels without formation of oxides. The diagram in Figure 1 was calculated using FactSage. This diagram shows that oxidation-reduction curves for Fe-18%Cr and Fe-18%Cr-8%Ni systems representing stainless steels are higher than the corresponding Cr/Cr₂O₃ curves. For alloys (e.g. steels), you can achieve more precise calculations using thermodynamic data from both the pure substances (i.e. pure metals and oxides) and solutions databases. Such diagrams can be produced specifically for the steels of interest and variety of atmosphere compositions.

These methods can help you troubleshoot and optimize your annealing operation by balancing hydrogen usage versus product quality.

Oxidation-reduction curves for pure chromium, Fe-18%Cr and Fe-18%Cr-8%Ni for the total pressure of 1 atm with a hydrogen partial pressure of 0.05 atm, corresponding N₂-5% H₂. (This diagram has been produced using thermodynamic data for solutions in addition to the data for pure elements and their oxides.)

Figure 1:

Vorming van oxidefilm is een functie van de verhouding van de partiële druk van waterstof/water, de temperatuur en de tijd, die allemaal aanzienlijk kunnen veranderen bij de uitgang van de oven. Een verhoogd dauwpunt als gevolg van het binnendringen van lucht met waterstof, gecombineerd met een verlaagde temperatuur, zal leiden tot oxidatie als de tijd in het uitgangsgebied voldoende lang is. Bovendien kan het ID-oppervlak van de slang langzamer afkoelen dan de OD, wat leidt tot inconsistente oxidatie. Tegenmaatregelen zijn onder meer het verhogen van de verplaatsingssnelheid van de slangen, het verhogen van het waterstofdebiet over alle slangoppervlakken en het aanbrengen van een stikstofgordijn bij de uitgang om het binnendringen van lucht te verdunnen en te helpen bij het koelen. Aan elke tegenmaatregel zijn technologische, veiligheids- en kostenoverwegingen verbonden.